dc.identifier.citationHOUDKOVÁ, Š., ČESÁNEK, Z., SMAZALOVÁ, E., LUKÁČ, F. The High-Temperature Wear and Oxidation Behavior of CrC-Based HVOF Coatings. JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2018, roč. 27, č. 1-2, s. 179-195. ISSN 1059-9630.en
dc.identifier.issn1059-9630
dc.identifier.uri2-s2.0-85029431754
dc.identifier.urihttp://hdl.handle.net/11025/29793
dc.description.abstractByly hodnoceny tři komerčně dostupné materiály na bázi CrC s rozdílnou matricí(Cr3C2-25%NiCr; Cr3C2-25%CoNiCrAlY and Cr3C2-50%NiCrMoNb), deponované pomocí technologie HVOF. Byla sledována jejich odolnost proti působení vyské teploty v různých typech prostředí - v horkém vzduchu a horké tlakové páře. Ukázalo se, že povlak Cr3C2-50%NiCrMoNb je vhodnou náhradou povlaku Cr3C2-25%NiC, který v prostředí horké tlakové páry podléhá preferenční oxidaci karbidických částic.cs
dc.format17 s.cs
dc.format.mimetypeapplication/pdf
dc.language.isoenen
dc.publisherSpringeren
dc.rightsPlný text není přístupný.cs
dc.rights© Springer Verlagen
dc.subjectHVOF, žárový nástřik, karbid chromu, oxidace, vysoká teplota, pára, opotřebení, energetikacs
dc.titleVysokoteplotní odolnost proti opotřebení a oxidaci HVOF povlaků na bázi CrCcs
dc.titleThe High-Temperature Wear and Oxidation Behavior of CrC-Based HVOF Coatingsen
dc.typečlánekcs
dc.typearticleen
dc.rights.accessclosedAccessen
dc.type.versionpublishedVersionen
dc.description.abstract-translatedThree commercially available chromium carbide-based powders with different kinds of matrix (Cr3C2-25%NiCr; Cr3C2-25%CoNiCrAlY and Cr3C2-50%NiCrMoNb) were deposited by an HVOF JP-5000 spraying gun, evaluated and compared. The influence of heat treatment on the microstructure and properties, as well as the oxidation resistance in a hot steam environment (p=24 MPa; T=609°C) were evaluated by SEM and XRD with respect to their potential application in the steam power industry. The sliding wear resistance measured at room and elevated (T=600°C) temperatures according to ASTM G-133. For all three kinds of chromium carbide-based coatings the precipitation of secondary carbides from the supersaturated matrix was observed during the heat treatment. For Cr3C2-25%NiCr coating annealed in hot steam environment as well as for Cr3C2-25%CoNiCrAlY coating in both environment, the inner carbide oxidation was recorded. The sliding wear resistance was found equal at room temperature, regardless of the matrix composition and content, while at elevated temperatures, the higher wear was measured, varying in dependence on the matrix composition and content. The chromium carbide-based coating with modified matrix composition Cr3C2-50%NiCrMoNb is suitable to replace the Cr3C2-25%NiCr coating in a hot steam environment to eliminate the risk of failure caused by inner carbide oxidationen
dc.subject.translatedHVOF, thermal spray, chromium carbide, oxidation, high temperature, wear, power industryen
dc.identifier.doi10.1007/s11666-017-0637-3
dc.type.statusPeer-revieweden
dc.identifier.document-number419001600017
dc.identifier.obd43922177
dc.project.IDTE01020068/Centrum výzkumu a experimnetálního vývoje spolehlivé energetikycs
Vyskytuje se v kolekcích:Články / Articles (CTM)
OBD

Soubory připojené k záznamu:
Soubor VelikostFormát 
The High-Temperature Wear and Oxidation Behaviour of CrC-Based HVOF Coatings.pdf4,04 MBAdobe PDFZobrazit/otevřít  Vyžádat kopii
Zobrazit minimální záznam Zobrazit statistiky


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/29793

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.

hledání
navigace
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD