dc.identifier.citationJENÍČEK, Š. PEKOVIĆ, M. OPATOVÁ, K. VOREL, I. Relationship between Mechanical Properties in 42SiCr and 42SiMn Medium-carbon Steels and Austempering Temperatures. Manufacturing Technology, 2021, roč. 21, č. 1, s. 71-75. ISSN 1213-2489.cs
dc.identifier.issn1213-2489
dc.identifier.uri2-s2.0-85102405590
dc.identifier.urihttp://hdl.handle.net/11025/43219
dc.description.abstractU konvenčních ocelí sestává bainitická mikrostruktura, která se tvoří za izotermických podmínek, z bainitického feritu a precipitátů karbidů, jejichž distribuce a velikost závisí na parametrech izotermického zpracování. U ocelí CFB (bezkarbidický bainit) jsou však hlavními mikrostrukturálními složkami bainitický ferit, zbytkový austenit, případně i M-A složka. CFB mikrostruktury mohou mít lepší tažnost a stejnou nebo dokonce vyšší pevnost než mikrostruktury bainitického feritu s precipitáty karbidů. Tato výhoda vyplývá z principu vzniku CFB mikrostruktury a souvisí s absencí křehkých karbidů a jejich substitucí zbytkovým austenitem. Tento článek zkoumá vliv austemperingu na mechanické vlastnosti nekonvenčních CFB ocelí 42SiCr a 42SiMn.cs
dc.format5 s.cs
dc.format.mimetypeapplication/pdf
dc.language.isoenen
dc.publisherJan Evangelista Purkyne Universityen
dc.relation.ispartofseriesManufacturing Technologyen
dc.rights© J. E. Purkyne Universityen
dc.subjectAustemperingcs
dc.subjectCFB strukturacs
dc.subjectKřemíkcs
dc.subjectMechanické vlastnostics
dc.titleRelationship between Mechanical Properties in 42SiCr and 42SiMn Medium-carbon Steels and Austempering Temperaturesen
dc.title.alternativeVztah mezi mechanickými vlastnostmi u 42SiCr a 42SiMn středouhlíkových ocelí a temperovacích teplotcs
dc.typečlánekcs
dc.typearticleen
dc.rights.accessopenAccessen
dc.type.versionpublishedVersionen
dc.description.abstract-translatedSheet metal forming boundaries are established using the forming limit diagram (FLD). The Nakajima and Marciniak tests, which are based on stretching a material using a punch, are the most commonly used methods for determining the FLD or fracture forming limit diagram (FFLD). The results are usually evaluated by calculating local strain, strain rates, specimen thickness reduction or fracture strain. When the amount of experimental material is insufficient, miniaturization of the testing specimens may be a solution. However, the interchangeability of the results for standard and miniaturized specimens has not been proven yet. In this study, the Nakajima tests were performed using standard and sub-sized specimens made of manganese–boron steel 22MnB5, commonly used in the automotive industry. Afterwards, four FLD/FFLD evaluation methods were applied and compared. The miniaturized specimens yielded higher strain values, which was explained by the varied ratio of material thickness/punch diameter and different bending conditions. The highest compliance of the results was recorded for the standard and miniaturized FFLDen
dc.subject.translatedAustemperingen
dc.subject.translatedCFB structureen
dc.subject.translatedSiliconen
dc.subject.translatedMechanical propertiesen
dc.identifier.doi10.21062/mft.2021.005
dc.type.statusPeer-revieweden
dc.identifier.obd43932704
dc.project.IDSGS-2018-045/Vývoj tepelného a termomechanického zpracování vysokopevných ocelí třetí generacecs
Vyskytuje se v kolekcích:Články / Articles (KMM)
Články / Articles (RTI)
OBD

Soubory připojené k záznamu:
Soubor VelikostFormát 
MT_mft-202101-0005.pdf546,97 kBAdobe PDFZobrazit/otevřít
Zobrazit minimální záznam Zobrazit statistiky


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/43219

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.

hledání
navigace
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD